Atlas™
Category: Waste Management > Waste Treatment > Misc-Treatment
Reference # : Model No :
Atlas™ is a high strength, high stiffness carbon fiber solution for on-site repair of pipeline and piping structures. Atlas™ is designed for repairs requiring strain reduction due to dynamic loading conditions.
The Atlas™ composite repair system is comprised of a bi-directional carbon fiber system and high-strength epoxy resin. Field saturated and applied, this carbon fiber system contours extremely well around any seam or girth welds when combined with high strength load transfer filler helping minimize the strain at the crack tip.
Benefits
•Site impregnated
•Resin part A and part B come to the field premeasured
•Structural fabric is impregnated in the field with conventional equipment
•Restores pipe to original strength
•Ideal application temperature up to 120 °F (49 °C)
Limitations
Tensile Strength
•151,000 (1,041) PSI, MPa
Tensile Modulus
•9.7 x 106, (66,879) PSI, MPa
Flexural Strength
•113,000 (779) PSI, MPa
Flexural Modulus
•9.1 x 106, (62,742) PSI, MPa
Shear Modulus
•9.64 x 105 (6,647) PSI, MPa
Interlaminar Shear Strength
•8,200 (56.5) PSI, MPa
Barcol Hardness
•53
Glass Transition
•350°F (177°C)
Thermal Expansion
•.116 um/m/°F (.208 um/m/°C)
Poisson's Ratio
•.150
Stocked Width
•12" (30.5 cm)
Fabric Orientation
•Bi-Axial 0° and 90°
Cure Ply Thickness
•0.019 IN (19 mils) (0.48 mm)
Maximum Operating Temperature
•314°F (157°C)
Working Time (Dependent on Temperature)
•40 Minutes @ Ambient
Set Time
•1 Hour
Chemical Resistance
•Gasoline, MEK, Acetone, Toluene, Ethyl alcohol and other hydrocarbons
Shelf Life
•2 years from ship date
Application Conditions
•Above 45°F (7°C) up to 120°F (49°C)